Тёмный налёт при сварке в аргоне

Тут грязи вроде нет, но есть перегрев.
--- добавлено: 7 ноя 2014 в 16:09 ---
Не огорчайтесь.

http://www.millerwelds.com/resources/articles/common-TIG-GTAW-welding-problems-visual-guide-graphic/
Figure 7A and 7B – Poor Color on Stainless

Figure 7A shows discoloration on a stainless steel weld caused by overheating, which not only affects a material’s color, but degrades its corrosion resistance and mechanical properties as well. Unfortunately, once this error is made, there is nothing that can be done to fix it except for scrapping the part and starting over. To prevent overheating, reduce amperage, slightly increase travel speed or shorten the arc length. If your welding equipment features pulsing capabilities, now is the time to learn how to use them. Pulsing reduces heat input, and it offers excellent control of the weld puddle. Figure 7B shows proper coloration of stainless.


Figure 7A: Poor color on stainless steel

 

Так я снял фаски чтоб хорошо проварить и дал побольше ампер чтоб хорошо заплавить. А на фото не грязь это а паста. Я втирал чтоб быстрей очистить швы, она потемнела и кажется будто детали грязные.

 

У нержавейки самая главная задница, от чего ее сложнее всего варить, это то что это СПЛАВ. Там куча разных металлов, и у всех их разная температура кипения. Люминь, титан, СТ3, итд, греть можно сколько угодно, даже если сварочная ванна проплпавится, можно заварить. С нержей опа. чуть перегрел, и уже не нержа а сплав непонятного состава, бо полезные для сплава элементы испарились.

 

ось так повинні виглядати шви після зварювання...

 

Красивый шов, это вы сваривали?

 

На Ютубі є канал https://www.youtube.com/user/weldingtipsandtricks дуже багато корисної інфи для зварки, мінус - він англійською мовою

 

Там дофигища образовательной информации. Достаточно вбить tig welding.